High Speed Steels.

Standard grade for High Speed Steels; owing to its balanced composition has good toughness and cutting performance, hence many applications.
HSS Containing cobalt content is a high performance steel with good cutting capability & ensures high red hardness and tempering retention. It is particularly suitable in thermal stress situations and for intermittent cutting.
High Speed Steel with high molybdenum and carbon. It has high wear resistance, high red hardness and good toughness. With its low vanadium content, this grade has very good grind ability

High performance Gear Cutting Hobs, Shapers, Milling cutters, Bevel tools, of all kinds of highly stressed twist bits and taps, shaped shear blades, for working high strength materials, broaches. Cutting tools for roughing or finishing, such as: helical bits, milling cutters of all types, taps, dies, spindles, reamers, thread rolling tools, drill bits, circular saw segments. Impact tools and those used for working wood. Cold forming tools such as dies and punches for cold extrusion and cutting and fine cutting tools.

Hardened Tempered Steel Strips.

These strips are available in the following specs:

Chemistry :
Chemical Composition
Grade %C %Si %Mn %S %P %Cr %V %Ni
C-65 0.60 -0.70 0.10.-0.35 0.50-0.65 0.05 0.05 – – –
C-80 0.75-0.85 0.10.-0.35 0.50-0.80 0.05 0.05 – – –
C-98 0.90-1.05 0.10.-0.35 0.50-0.80 0.05 0.05 – – –
50Cr4V2 0.45-0.55 0.10.-0.35 0.60-0.90 0.05 0.05 0.90-1.2 0.15-0.30 –
75Ni8 0.75-0.85 0.10.-0.35 0.50-0.80 0.05 0.05 – – 1.72-2.10

Kindly visit us at, www.btstrips.com , for a detailed knowledge of the product range.

Medium Carbon Steel Strips

Meduim Carbon Steels are similar to low carbon steel except that the carbon ranges from 0.30 to 0.60% & the manganese from 0.50 to 1.65%. Increasing the carbon content is approximately 0.5% with an accompanying increase in manganese allows medium carbon steels to be used in the quenched & tempered conditions. This steels are of particular importance because of unique combination of strength & toughness after heat treat treatment.